Влияние температуры нагружения на неупругие эффекты в двойном сплаве TI[49.2]NI[50.8](АТ. %); Материалы и технологии новых поколений в современном материаловедении
| Parent link: | Материалы и технологии новых поколений в современном материаловедении.— 2015.— [С. 61-64] |
|---|---|
| 第一著者: | |
| 団体著者: | |
| その他の著者: | , |
| 要約: | Заглавие с титульного экрана The data about the supelasticity (SE) and shape memory effect (SME) under torsion of the samples of Ti[49.2]Ni[50.8](at. %) alloy after the isothermal loading inside the 285-346K temperature range are presented. The dependences of SE, SME and the plastic deformation (VS) the torsional strain under isothermal loading are obtained. The reversible martensitic deformation are analyzed using the idea about equivalent deformations under tension and torsion tests. The abnormally high recovery deformations exceeded the crystallography resource of recovery deformation (CRRD) about 4.5% was found after loading at 296K (below TR; TR is the temperature of the R phase formation ). The recovery deformations decrease to (or less) CRRD with the increase of loading temperature about 15-30 degree above TR. |
| 言語: | ロシア語 |
| 出版事項: |
2015
|
| シリーズ: | Проблемы прочности современных конструкционных материалов |
| 主題: | |
| オンライン･アクセス: | http://earchive.tpu.ru/handle/11683/18292 http://www.lib.tpu.ru/fulltext/c/2015/C39/013.pdf |
| フォーマット: | 電子媒体 図書の章 |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=616392 |
MARC
| LEADER | 00000naa2a2200000 4500 | ||
|---|---|---|---|
| 001 | 616392 | ||
| 005 | 20231101132915.0 | ||
| 035 | |a (RuTPU)RU\TPU\conf\14630 | ||
| 035 | |a RU\TPU\conf\14629 | ||
| 090 | |a 616392 | ||
| 100 | |a 20151224d2015 k y0rusy50 ca | ||
| 101 | 0 | |a rus |d eng | |
| 102 | |a RU | ||
| 105 | |a y z 101zy | ||
| 135 | |a drgn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Влияние температуры нагружения на неупругие эффекты в двойном сплаве TI[49.2]NI[50.8](АТ. %) |d Effect of the loading temperature on inelastic effects in binary TI[49.2]NI[50.8](АТ. %) alloy |f Т. Н. Пятова, Д. Ю. Жапова, В. Н. Гришков | |
| 203 | |a Текст |c электронный | ||
| 225 | 1 | |a Проблемы прочности современных конструкционных материалов | |
| 230 | |a 1 компьютерный файл (pdf; 378 Кб) | ||
| 300 | |a Заглавие с титульного экрана | ||
| 320 | |a [Библиогр.: с. 64 (3 назв.)] | ||
| 330 | |a The data about the supelasticity (SE) and shape memory effect (SME) under torsion of the samples of Ti[49.2]Ni[50.8](at. %) alloy after the isothermal loading inside the 285-346K temperature range are presented. The dependences of SE, SME and the plastic deformation (VS) the torsional strain under isothermal loading are obtained. The reversible martensitic deformation are analyzed using the idea about equivalent deformations under tension and torsion tests. The abnormally high recovery deformations exceeded the crystallography resource of recovery deformation (CRRD) about 4.5% was found after loading at 296K (below TR; TR is the temperature of the R phase formation ). The recovery deformations decrease to (or less) CRRD with the increase of loading temperature about 15-30 degree above TR. | ||
| 337 | |a Adobe Reader | ||
| 463 | 0 | |0 (RuTPU)RU\TPU\conf\14276 |t Материалы и технологии новых поколений в современном материаловедении |o сборник трудов Международной конференции с элементами научной школы для молодежи, г. Томск, 9 – 11 ноября 2015 г. |f Национальный исследовательский Томский политехнический университет (ТПУ) ; Академия наук СССР (АН СССР), Сибирское отделение (СО), Институт физики прочности и материаловедения (ИФПМ) ; Российский фонд фундаментальных исследований (РФФИ) |v [С. 61-64] |d 2015 | |
| 510 | 1 | |a Effect of the loading temperature on inelastic effects in binary TI[49.2]NI[50.8](АТ. %) alloy |z eng | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a температура | |
| 610 | 1 | |a нагружение | |
| 610 | 1 | |a неупругие эффекты | |
| 610 | 1 | |a сплавы | |
| 610 | 1 | |a никелид титана | |
| 700 | 1 | |a Пятова |b Т. Н. | |
| 701 | 1 | |a Жапова |b Д. Ю. | |
| 701 | 1 | |a Гришков |b В. Н. | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет (ТПУ) |c (2009- ) |2 stltpush |3 (RuTPU)RU\TPU\col\15902 |
| 801 | 2 | |a RU |b 63413507 |c 20210209 |g RCR | |
| 856 | 4 | |u http://earchive.tpu.ru/handle/11683/18292 | |
| 856 | 4 | |u http://www.lib.tpu.ru/fulltext/c/2015/C39/013.pdf | |
| 942 | |c BK | ||