Позитронная спектроскопия дефектной структуры в насыщенном водородом цирконии; Материалы и технологии новых поколений в современном материаловедении
| Parent link: | Материалы и технологии новых поколений в современном материаловедении.— 2015.— [С. 11-15] |
|---|---|
| Autor Corporativo: | |
| Outros autores: | , , , |
| Summary: | Заглавие с титульного экрана Zirconium alloys, such as Zr-1Nb are widely used as cladding materials for nuclear fuel elements of light water reactors. Hydrogen embrittlement problem causes degradation of these parts of nuclear reactors. It is known, that hydrogen uptake causes changes in microstructure and defect structure of metals. The aim of this work is study of Zr-1Nb alloys' defect structure after hydrogen saturation up to the concentration of 600 ppm. Saturation of hydrogen was carried out from the gas phase under high temperature and pressure. This study reveals the increase of average positron lifetime with the increase of hydrogen concentration. Value of the average positron lifetime achieves plateau when the concentration of hydrogen is about 300 ppm. Also the following effects were detected in the material after hydrogen uptake up to different concentrations: crystal lattice expansion, dislocations and vacancy-like defects formation, as well as the defect-hydrogen complexes formation. |
| Idioma: | ruso |
| Publicado: |
2015
|
| Series: | Проблемы прочности современных конструкционных материалов |
| Subjects: | |
| Acceso en liña: | http://earchive.tpu.ru/handle/11683/18255 http://www.lib.tpu.ru/fulltext/c/2015/C39/001.pdf |
| Formato: | Electrónico Capítulo de libro |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=616373 |
MARC
| LEADER | 00000naa2a2200000 4500 | ||
|---|---|---|---|
| 001 | 616373 | ||
| 005 | 20260618152003.0 | ||
| 035 | |a (RuTPU)RU\TPU\conf\14611 | ||
| 035 | |a RU\TPU\conf\14581 | ||
| 090 | |a 616373 | ||
| 100 | |a 20151224d2015 k y0rusy50 ca | ||
| 101 | 0 | |a rus | |
| 102 | |a RU | ||
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Позитронная спектроскопия дефектной структуры в насыщенном водородом цирконии |d Positron spectroscopy of defect structure in ydrogensaturated zirconium |f Ю. С. Бордулёв [и др.] | |
| 203 | |a Текст |c электронный | ||
| 225 | 1 | |a Проблемы прочности современных конструкционных материалов | |
| 300 | |a Заглавие с титульного экрана | ||
| 320 | |a [Библиогр.: с. 14-15 (23 назв.)] | ||
| 330 | |a Zirconium alloys, such as Zr-1Nb are widely used as cladding materials for nuclear fuel elements of light water reactors. Hydrogen embrittlement problem causes degradation of these parts of nuclear reactors. It is known, that hydrogen uptake causes changes in microstructure and defect structure of metals. The aim of this work is study of Zr-1Nb alloys' defect structure after hydrogen saturation up to the concentration of 600 ppm. Saturation of hydrogen was carried out from the gas phase under high temperature and pressure. This study reveals the increase of average positron lifetime with the increase of hydrogen concentration. Value of the average positron lifetime achieves plateau when the concentration of hydrogen is about 300 ppm. Also the following effects were detected in the material after hydrogen uptake up to different concentrations: crystal lattice expansion, dislocations and vacancy-like defects formation, as well as the defect-hydrogen complexes formation. | ||
| 337 | |a Adobe Reader | ||
| 463 | 1 | |0 (RuTPU)RU\TPU\conf\14276 |t Материалы и технологии новых поколений в современном материаловедении |o сборник трудов Международной конференции с элементами научной школы для молодежи, г. Томск, 9 – 11 ноября 2015 г. |f Национальный исследовательский Томский политехнический университет (ТПУ) ; Академия наук СССР (АН СССР), Сибирское отделение (СО), Институт физики прочности и материаловедения (ИФПМ) ; Российский фонд фундаментальных исследований (РФФИ) |v [С. 11-15] |d 2015 | |
| 510 | 1 | |a Positron spectroscopy of defect structure in ydrogensaturated zirconium |z eng | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a позитронная спектроскопия | |
| 610 | 1 | |a спектроскопия | |
| 610 | 1 | |a дефектные структуры | |
| 610 | 1 | |a водород | |
| 610 | 1 | |a цирконий | |
| 610 | 1 | |a циркониевые сплавы | |
| 610 | 1 | |a ядерные реакторы | |
| 610 | 1 | |a сплавы | |
| 610 | 1 | |a дефекты | |
| 701 | 1 | |a Бордулёв |b Ю. С. |c физик |c инженер Томского политехнического университета |f 1990- |g Юрий Сергеевич |3 (RuTPU)RU\TPU\pers\29925 | |
| 701 | 1 | |a Ли |b К. | |
| 701 | 1 | |a Лаптев |b Р. С. |c физик, специалист в области неразрушающего контроля |c доцент Томского политехнического университета, доктор технических наук |f 1987- |g Роман Сергеевич |3 (RuTPU)RU\TPU\pers\29924 |9 14396 | |
| 701 | 1 | |a Кудияров |b В. Н. |c физик |c доцент Томского политехнического университета, кандидат технических наук |f 1990- |g Виктор Николаевич |3 (RuTPU)RU\TPU\pers\30612 |9 14893 | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет (ТПУ) |b Физико-технический институт (ФТИ) |b Кафедра общей физики (ОФ) |3 (RuTPU)RU\TPU\col\18734 |
| 801 | 2 | |a RU |b 63413507 |c 20210209 |g RCR | |
| 856 | 4 | |u http://earchive.tpu.ru/handle/11683/18255 | |
| 856 | 4 | |u http://www.lib.tpu.ru/fulltext/c/2015/C39/001.pdf | |
| 942 | |c BK | ||