Исследование ультрадисперсных оксидов меди, полученных плазмодинамическим методом; Перспективы развития фундаментальных наук
| Parent link: | Перспективы развития фундаментальных наук.— 2015.— [С. 1140-1142] |
|---|---|
| Autore principale: | |
| Ente Autore: | |
| Altri autori: | , , |
| Riassunto: | Заглавие с экрана The synthesis of copper oxides has a great importance due to the fact these materials are widely used in superconductors manufacturing. It’s known that properties of materials in nanodispersed conditions are improved. In this article, an analysis of ultradispersed plasmodynamic synthesis product obtained using coaxial magnetoplasma accelerator with copper electrodes was carried out. The obtained powder was analyzed by X-ray diffractometer Shimadzu XRD 7000 using the temperature consoles Anton Paar TTK450. Using this analysis such phases as copper Cu, copper oxide (I) Cu2O, copper oxide (II) CuO, and copper hydroxide hydrate Cu(OH)[2]•H[2]O were identified in the product. By gradually heating, the powder to the temperature of 800 °С the phase change was observed. The mass of copper oxide increased up to 96% and copper hydroxide hydrate. |
| Lingua: | russo |
| Pubblicazione: |
2015
|
| Serie: | Наноматериалы и нанотехнологии |
| Soggetti: | |
| Accesso online: | http://earchive.tpu.ru/handle/11683/19090 http://www.lib.tpu.ru/fulltext/c/2015/C21/363.pdf |
| Natura: | Elettronico Capitolo di libro |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=613201 |
MARC
| LEADER | 00000naa2a2200000 4500 | ||
|---|---|---|---|
| 001 | 613201 | ||
| 005 | 20231226163448.0 | ||
| 035 | |a (RuTPU)RU\TPU\conf\11333 | ||
| 035 | |a RU\TPU\conf\11288 | ||
| 090 | |a 613201 | ||
| 100 | |a 20150708d2015 k y0rusy50 ca | ||
| 101 | 0 | |a rus | |
| 102 | |a RU | ||
| 105 | |a a z 101zy | ||
| 135 | |a drgn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Исследование ультрадисперсных оксидов меди, полученных плазмодинамическим методом |d Study of ultradispersed copper oxides obtained by plasmodynamic method |f Ю. Л. Шаненкова, И. И. Шаненков |g науч. рук. А. А. Сивков, А. С. Сайгаш | |
| 203 | |a Текст |c электронный | ||
| 215 | |a 1 файл(414 Кб) | ||
| 225 | 1 | |a Наноматериалы и нанотехнологии | |
| 300 | |a Заглавие с экрана | ||
| 320 | |a [Библиогр.: с. 1142 (4 назв.)] | ||
| 330 | |a The synthesis of copper oxides has a great importance due to the fact these materials are widely used in superconductors manufacturing. It’s known that properties of materials in nanodispersed conditions are improved. In this article, an analysis of ultradispersed plasmodynamic synthesis product obtained using coaxial magnetoplasma accelerator with copper electrodes was carried out. The obtained powder was analyzed by X-ray diffractometer Shimadzu XRD 7000 using the temperature consoles Anton Paar TTK450. Using this analysis such phases as copper Cu, copper oxide (I) Cu2O, copper oxide (II) CuO, and copper hydroxide hydrate Cu(OH)[2]•H[2]O were identified in the product. By gradually heating, the powder to the temperature of 800 °С the phase change was observed. The mass of copper oxide increased up to 96% and copper hydroxide hydrate. | ||
| 337 | |a Adobe Reader | ||
| 463 | 1 | |0 (RuTPU)RU\TPU\conf\10376 |t Перспективы развития фундаментальных наук |l Prospects of fundamental sciences development |o сборник научных трудов XII Международной конференция студентов и молодых ученых, г. Томск, 21-24 апреля 2015 г. |f Национальный исследовательский Томский политехнический университет (ТПУ) ; Национальный исследовательский Томский государственный университет (ТГУ) ; Томский государственный архитектурно-строительный университет (ТГАСУ) ; Томский государственный университет систем управления и радиоэлектроники (ТУСУР) ; ред. кол. И. А. Курзина ; Г. А. Воронова ; С. А. Поробова |v [С. 1140-1142] |d 2015 | |
| 510 | 1 | |a Study of ultradispersed copper oxides obtained by plasmodynamic method |z eng | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a ультрадисперсные оксиды | |
| 610 | 1 | |a медь | |
| 610 | 1 | |a плазмодинамические методы | |
| 700 | 1 | |a Шаненкова |b Ю. Л. |c специалист в области электроэнергетики |c доцент Томского политехнического университета, кандидат технических наук |f 1991- |g Юлия Леонидовна |3 (RuTPU)RU\TPU\pers\34117 |9 17657 | |
| 701 | 1 | |a Шаненков |b И. И. |c специалист в области электроэнергетики |c доцент Томского политехнического университета, кандидат наук |f 1990- |g Иван Игоревич |3 (RuTPU)RU\TPU\pers\31744 |9 15856 | |
| 702 | 1 | |a Сивков |b А. А. |c специалист в области электроэнергетики |c профессор Томского политехнического университета, доктор технических наук |f 1951- |g Александр Анатольевич |4 727 | |
| 702 | 1 | |a Сайгаш |b А. С. |c специалист в области электроэнергетики |c доцент Томского политехнического университета, кандидат технических наук |f 1981- |g Анастасия Сергеевна |4 727 | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет (ТПУ) |b Энергетический институт (ЭНИН) |b Кафедра электроснабжения промышленных предприятий (ЭПП) |3 (RuTPU)RU\TPU\col\18676 |
| 801 | 1 | |a RU |b 63413507 |c 20101016 | |
| 801 | 2 | |a RU |b 63413507 |c 20210128 |g RCR | |
| 856 | 4 | |u http://earchive.tpu.ru/handle/11683/19090 | |
| 856 | 4 | |u http://www.lib.tpu.ru/fulltext/c/2015/C21/363.pdf | |
| 942 | |c BK | ||