| Parent link: | Перспективы развития фундаментальных наук=Prospects of fundamental sciences development: сборник научных трудов XI Международной конференция студентов и молодых ученых, г. Томск, 22-25 апреля 2014 г./ Национальный исследовательский Томский политехнический университет (ТПУ) ; под ред. Е. А. Вайтулевич. [С. 989-991].— , 2014 |
|---|---|
| Hovedforfatter: | |
| Institution som forfatter: | |
| Andre forfattere: | , , |
| Summary: | Заглавие с экрана This report covers properties of ceramics produced in the system Ti-Si-N, by SPS. Hardness and fracture toughness were measured. In this research the raw material was produced by a direct synthesis in the hypersonic high-current electrical discharge plasma arc obtained using a coaxial magneto-plasma accelerator (CMPA). The phase composition of the raw material and the obtained ceramics were explored. Ceramics has the high mean value of hardness (about 20 GPa), the elastic modulus (about 333 GPa) and the fracture toughness (about K[1С]=9,03 MPa•m{1/2}). |
| Udgivet: |
2014
|
| Serier: | Наноматериалы и нанотехнологии |
| Fag: | |
| Online adgang: | http://www.lib.tpu.ru/fulltext/c/2014/C21/334.pdf |
| Format: | Electronisk Book Chapter |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=607051 |
| Fysisk beskrivelse: | 1 файл(476 Кб) |
|---|---|
| Summary: | Заглавие с экрана This report covers properties of ceramics produced in the system Ti-Si-N, by SPS. Hardness and fracture toughness were measured. In this research the raw material was produced by a direct synthesis in the hypersonic high-current electrical discharge plasma arc obtained using a coaxial magneto-plasma accelerator (CMPA). The phase composition of the raw material and the obtained ceramics were explored. Ceramics has the high mean value of hardness (about 20 GPa), the elastic modulus (about 333 GPa) and the fracture toughness (about K[1С]=9,03 MPa•m{1/2}). |