Изучение структурно-фазовых превращений в аустенитной стали Х18Н10Т при комбинировании прокатки с легированием водородом; Перспективы развития фундаментальных наук

Chi tiết về thư mục
Parent link:	Перспективы развития фундаментальных наук.— 2013.— [С. 108-110]
Tác giả chính:	Кретов Ю. Л.
Tác giả khác:	Мельников Е. В. (научный руководитель), Майер Г. Г., Астафурова Е. Г. Елена Геннадьевна
Tóm tắt:	Заглавие с экрана The influence of a combination of rolling and reversible hydrogenation on the structural and phase transformations in Fe-18Cr-10Ni-1Ti (in wt. %) austenitic stainless steel was studied. Electrolytic hydrogen saturation and subsequent rolling increases the amount of α-phase in steel under investigation. Analysis of the phase composition of the samples showed that the hydrogen alloying also contributes to the appearance of -martensite in the structure of steel. Microhardness increases slightly with increasing hydrogenation time and current density.
Ngôn ngữ:	Tiếng Nga
Được phát hành:	2013
Loạt:	Физика
Những chủ đề:	электронный ресурс труды учёных ТПУ структурно-фазовые превращения аустенитные стали комбинирование прокатка легирование водород
Truy cập trực tuyến:	http://www.lib.tpu.ru/fulltext/c/2013/C21/031.pdf
Định dạng:	Điện tử Chương của sách
KOHA link:	https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=603574

Internet