Evaluating the effectiveness of the process of hydration and hardening of hydraulic binders magnesia with simultaneous thermal analysis; International Conference on Thermal Analysis and Calorimetry in Russia (RTAC-2016); Vol. 1
| Parent link: | International Conference on Thermal Analysis and Calorimetry in Russia (RTAC-2016): 16-23 September, 2016 Saint-Petersburg, Russia : proceeding.— , 2016 Vol. 1.— 2016.— P. 296-300 |
|---|---|
| Autor principal: | |
| Autor Corporativo: | |
| Otros Autores: | , |
| Sumario: | The article presents the results of the study of structure waterproof hydraulic magnesia binder in the process of hydration and hardening. Studies conducted using the combined thermal analysis (TG / DTA). It is shown that the process of curing in humid conditions hydrocarbonate of magnesia binder is most effective due to the increase of hydrocarbon products, which was an increase of peaks at 405.4 ° C in curves TG/DTA. В статье представлены результаты исследования структурообразования водостойкого гидравлического магнезиального вяжущего в процессе гидратации и твердения. Исследования проведены с помощью совмещенного термического анализа (ТГ/ДТА). Показано, что процесс твердения во влажных условиях гидрокарбонатного магнезиального вяжущего наиболее эффективен вследствие увеличения гидрокарбонатных продуктов, что отмечено увеличением пиков при 405,4°С на кривых ТГ/ДТА. В фонде НТБ ТПУ отсутствует |
| Lenguaje: | ruso |
| Publicado: |
2016
|
| Colección: | Section 1: Thermal analysis and calorimetry of inorganic substances and materials |
| Materias: | |
| Formato: | Capítulo de libro |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=602788 |
| Sumario: | The article presents the results of the study of structure waterproof hydraulic magnesia binder in the process of hydration and hardening. Studies conducted using the combined thermal analysis (TG / DTA). It is shown that the process of curing in humid conditions hydrocarbonate of magnesia binder is most effective due to the increase of hydrocarbon products, which was an increase of peaks at 405.4 ° C in curves TG/DTA. В статье представлены результаты исследования структурообразования водостойкого гидравлического магнезиального вяжущего в процессе гидратации и твердения. Исследования проведены с помощью совмещенного термического анализа (ТГ/ДТА). Показано, что процесс твердения во влажных условиях гидрокарбонатного магнезиального вяжущего наиболее эффективен вследствие увеличения гидрокарбонатных продуктов, что отмечено увеличением пиков при 405,4°С на кривых ТГ/ДТА. В фонде НТБ ТПУ отсутствует |
|---|