Coating deposition using vacuum arc and ablation metal plasma; Surface and Coatings Technology; Vol. 203, № 17-18
| Parent link: | Surface and Coatings Technology.— , 2004- Vol. 203, № 17-18.— 2009.— P. 2735-2738 |
|---|---|
| Hlavní autor: | |
| Další autoři: | , |
| Shrnutí: | An innovative concept in the development of advanced coating deposition and ion implantation method including an application of filtered DC metal plasma or ablation plasma and high-frequency short-pulsed negative bias voltage with a duty factor in the range 10-99% is considered. The regularities of metal ion implantation and vacuum arc metal plasma or ablation plasma deposition for conducting and insulating materials are considered. It was shown that plasma based ion implantation as well as high-concentration plasma ion implantation with compensation of ion surface sputtering by plasma deposition as well as ion-assisted coating deposition may be realized for metal and dielectric samples by variation of negative bias potential in the range of 0-4·103 V, pulse repetition rate smoothly adjusted in the range of (2-4.4) × 105 pps and pulse duration in the range of 0.5-2 μs. It was experimentally shown that at coating deposition from ablation plasma obtained by high intensity ion beam (j = 300 A/cm2, E = 350 keV, τ = 90 ns) influence on the target, the breakdown of the plasma sheet occurred at dc negative bias potential on a substrate more than 60 V. The transfer to 0.5 μs duration pulses allowed us to increase the bias potential up to - 4 kV. The possibility of high-frequency, short-pulsed plasma-immersion ion implantation and deposition method application for coating deposition from vacuum arc and ablation plasma with high adhesive strength and improved exploitation characteristics is discussed in the paper. В фонде НТБ ТПУ отсутствует |
| Jazyk: | angličtina |
| Vydáno: |
2009
|
| Témata: | |
| Médium: | Kapitola |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=599627 |
MARC
| LEADER | 00000naa0a2200000 4500 | ||
|---|---|---|---|
| 001 | 599627 | ||
| 005 | 20250121112344.0 | ||
| 035 | |a (RuTPU)RU\TPU\tpu\23733 | ||
| 035 | |a RU\TPU\tpu\20385 | ||
| 090 | |a 599627 | ||
| 100 | |a 20131010d2009 k||y0rusy50 ba | ||
| 101 | 0 | |a eng | |
| 102 | |a NL | ||
| 200 | 1 | |a Coating deposition using vacuum arc and ablation metal plasma |f A. I. Ryabchikov, V. M. Matvienko, I. B. Stepanov | |
| 320 | |a References: 33 tit. | ||
| 330 | |a An innovative concept in the development of advanced coating deposition and ion implantation method including an application of filtered DC metal plasma or ablation plasma and high-frequency short-pulsed negative bias voltage with a duty factor in the range 10-99% is considered. The regularities of metal ion implantation and vacuum arc metal plasma or ablation plasma deposition for conducting and insulating materials are considered. It was shown that plasma based ion implantation as well as high-concentration plasma ion implantation with compensation of ion surface sputtering by plasma deposition as well as ion-assisted coating deposition may be realized for metal and dielectric samples by variation of negative bias potential in the range of 0-4·103 V, pulse repetition rate smoothly adjusted in the range of (2-4.4) × 105 pps and pulse duration in the range of 0.5-2 μs. It was experimentally shown that at coating deposition from ablation plasma obtained by high intensity ion beam (j = 300 A/cm2, E = 350 keV, τ = 90 ns) influence on the target, the breakdown of the plasma sheet occurred at dc negative bias potential on a substrate more than 60 V. The transfer to 0.5 μs duration pulses allowed us to increase the bias potential up to - 4 kV. The possibility of high-frequency, short-pulsed plasma-immersion ion implantation and deposition method application for coating deposition from vacuum arc and ablation plasma with high adhesive strength and improved exploitation characteristics is discussed in the paper. | ||
| 333 | |a В фонде НТБ ТПУ отсутствует | ||
| 461 | |t Surface and Coatings Technology |d 2004- | ||
| 463 | |t Vol. 203, № 17-18 |v P. 2735-2738 |d 2009 | ||
| 610 | 1 | |a труды учёных ТПУ | |
| 700 | 1 | |a Ryabchikov |b A. I. |c Professor of Tomsk Polytechnic University, Doctor of physical and mathematical sciences |c physicist |f 1950- |g Aleksandr Ilyich |3 (RuTPU)RU\TPU\pers\30912 | |
| 701 | 1 | |a Matvienko |b V. M. | |
| 701 | 1 | |a Stepanov |b I. B. | |
| 801 | 1 | |a RU |b 63413507 |c 20111213 | |
| 801 | 2 | |a RU |b 63413507 |c 20131010 |g RCR | |
| 942 | |c CR | ||