On the nature of the silver phases of Ag/Al2O3 catalysts for reactions involving nitric oxide; Applied Catalysis B: Environmental; Vol. 36, iss. 4

On the nature of the silver phases of Ag/Al2O3 catalysts for reactions involving nitric oxide; Applied Catalysis B: Environmental; Vol. 36, iss. 4

Detaylı Bibliyografya
Parent link:Applied Catalysis B: Environmental.— , 1992-
Vol. 36, iss. 4.— 2002.— P. 287-297
Diğer Yazarlar: Bogdanchikova N., Meunier F. C., Avalos-Borja M., Breen J. P., Pestryakov A. N. Aleksey Nikolaevich
Özet:The nature of the silver phases of Ag/Al2O3 catalysts (prepared by silver nitrate impregnation followed by calcination) was investigated by X-ray diffractograms (XRD), transmission electron microscopy (TEM) and UV–VIS analyses and related to the activity of the corresponding materials for the oxidation of NO to NO2. The UV–VIS spectrum of the 1.2 wt.% Ag/Al2O3 exhibited essentially one band associated with Ag+ species and the NO2 yields measured over this material were negligible. A 10 wt.% Ag/Al2O3 material showed the presence of oxidic species of silver (as isolated Ag+ cations and silver aluminate), but the UV–VIS data also revealed the presence of some metallic silver. The activity for the NO oxidation to NO2 of this sample was moderate. The same 10% sample either reduced in H2 or used for the C3H6-selective catalytic reduction (SCR) of NO showed a significantly larger proportion of silver metallic phases and these samples displayed a high activity for the formation of NO2. These data show that the structure and nature of the silver phases of Ag/Al2O3 catalysts can markedly change under reaction feed containing only a fraction of reducing agent (i.e. 500 ppm of propene) in net oxidizing conditions (2.5% O2). The low activity for N2 formation during the C3H6-SCR of NO (reported in an earlier study) over the high loading sample can, therefore, be related to the presence of metallic silver, which is yet a good catalyst for NO oxidation to NO2. The reverse observations apply for the oxide species observed over the low loading sample, which is a good SCR catalyst but do not oxidize NO to NO2.
В фонде НТБ ТПУ отсутствует
Dil:İngilizce
Baskı/Yayın Bilgisi: 2002
Konular:
труды учёных ТПУ
Materyal Türü: Kitap Bölümü
KOHA link:https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=599056

Benzer Materyaller

Benzer Materyaller