Phase composition of the products of nitriding ferrosilicon with zircon concentrate additives; Glass and Ceramics; Vol. 65, N 1-2

Dades bibliogràfiques
Parent link:	Glass and Ceramics.— , 2008 Vol. 65, N 1-2.— 2008.— P. 38-40
Autor principal:	Chukhlomina L. N.
Altres autors:	Vitushkina O. G., Golobokov N. N., Vereshchagin (Vereschagin, Vereshagin) V. I. Vladimir Ivanovich
Sumari:	The process of nitride formation during combustion of iron silicon with the addition of zircon concentrate in nitrogen gas is investigated. It is determined that in the presence of zircon (5-70%) ferrosilicon burns in a surface regime, and the products of combustion are multiphase. For the optimal parameters of synthesis (nitrogen pressure 4-7 MPa and sample diameter 35-40 mm) the products of combustion are a composition consisting of a ceramic constituent (Si3N4-ZrO2-Si2N2O) and iron (α-Fe). The method of acidic enrichment is used to obtain a composite ceramic powder with iron mass content 0.5% В фонде НТБ ТПУ отсутствует
Idioma:	anglès
Publicat:	2008
Matèries:	труды учёных ТПУ
Format:	Capítol de llibre
KOHA link:	https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=596006

MARC


LEADER	00000naa0a2200000 4500
001	596006
005	20250324114201.0
035			\|a (RuTPU)RU\TPU\tpu\17977
035			\|a RU\TPU\tpu\17973
090			\|a 596006
100			\|a 20100903d2008 k\|\|y0rusy50 ba
101	0		\|a eng
102			\|a US
200	1		\|a Phase composition of the products of nitriding ferrosilicon with zircon concentrate additives \|f L. N. Chukhlomina [et al.]
320			\|a References: p. 40
330			\|a The process of nitride formation during combustion of iron silicon with the addition of zircon concentrate in nitrogen gas is investigated. It is determined that in the presence of zircon (5-70%) ferrosilicon burns in a surface regime, and the products of combustion are multiphase. For the optimal parameters of synthesis (nitrogen pressure 4-7 MPa and sample diameter 35-40 mm) the products of combustion are a composition consisting of a ceramic constituent (Si3N4-ZrO2-Si2N2O) and iron (α-Fe). The method of acidic enrichment is used to obtain a composite ceramic powder with iron mass content 0.5%
333			\|a В фонде НТБ ТПУ отсутствует
461			\|t Glass and Ceramics \|d 2008
463			\|t Vol. 65, N 1-2 \|v P. 38-40 \|d 2008
610	1		\|a труды учёных ТПУ
700		1	\|a Chukhlomina \|b L. N.
701		1	\|a Vitushkina \|b O. G.
701		1	\|a Golobokov \|b N. N.
701		1	\|a Vereshchagin (Vereschagin, Vereshagin) \|b V. I. \|c Chemical Engineer \|c Professor of Tomsk Polytechnic University, Doctor of technical sciences \|f 1942- \|g Vladimir Ivanovich \|3 (RuTPU)RU\TPU\pers\26325 \|9 12080
801		1	\|a RU \|b 63413507 \|c 20100831
801		2	\|a RU \|b 63413507 \|c 20120523 \|g RCR
942			\|c CR