Assessment of the compositions and components for obtaining foam-glass-crystalline materials from aluminosilicate initial materials; Glass and Ceramics; Vol. 66, N 3-4
| Parent link: | Glass and Ceramics.— , 2009 Vol. 66, N 3-4.— 2009.— P. 82-85 |
|---|---|
| Auteur principal: | |
| Autres auteurs: | , |
| Résumé: | The compositions suitable for obtaining foam-glass-crystalline materials from aluminosilicate initial materials (for the example of zeolite and greenstone) by means of a dual-stage technology at temperatures not exceeding 900°C are examined. The assessment criteria for the initial materials and compositions of the glass granulate are determined. It is shown that under the established conditions aluminosilicate initial material makes it possible to obtain foam-glass-crystalline material with density 250-350 kg/m3 and compression strength up to 2 MPa В фонде НТБ ТПУ отсутствует |
| Langue: | anglais |
| Publié: |
2009
|
| Sujets: | |
| Format: | Chapitre de livre |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=595998 |
MARC
| LEADER | 00000naa0a2200000 4500 | ||
|---|---|---|---|
| 001 | 595998 | ||
| 005 | 20250324112424.0 | ||
| 035 | |a (RuTPU)RU\TPU\tpu\17968 | ||
| 035 | |a RU\TPU\tpu\17964 | ||
| 090 | |a 595998 | ||
| 100 | |a 20100901d2009 k||y0rusy50 ba | ||
| 101 | 0 | |a eng | |
| 102 | |a US | ||
| 200 | 1 | |a Assessment of the compositions and components for obtaining foam-glass-crystalline materials from aluminosilicate initial materials |f O. V. Kaz'mina, V. I. Vereshchagin, A. N. Abiyaka | |
| 320 | |a References: p. 85 | ||
| 330 | |a The compositions suitable for obtaining foam-glass-crystalline materials from aluminosilicate initial materials (for the example of zeolite and greenstone) by means of a dual-stage technology at temperatures not exceeding 900°C are examined. The assessment criteria for the initial materials and compositions of the glass granulate are determined. It is shown that under the established conditions aluminosilicate initial material makes it possible to obtain foam-glass-crystalline material with density 250-350 kg/m3 and compression strength up to 2 MPa | ||
| 333 | |a В фонде НТБ ТПУ отсутствует | ||
| 461 | |t Glass and Ceramics |d 2009 | ||
| 463 | |t Vol. 66, N 3-4 |v P. 82-85 |d 2009 | ||
| 610 | 1 | |a труды учёных ТПУ | |
| 700 | 1 | |a Kazmina |b O. V. |c Chemical Engineer |c Professor of Tomsk Polytechnic University, Doctor of technical sciences |f 1967- |g Olga Viktorovna |9 16846 | |
| 701 | 1 | |a Vereshchagin (Vereschagin, Vereshagin) |b V. I. |c Chemical Engineer |c Professor of Tomsk Polytechnic University, Doctor of technical sciences |f 1942- |g Vladimir Ivanovich |3 (RuTPU)RU\TPU\pers\26325 |9 12080 | |
| 701 | 1 | |a Abiyaka |b A. N. | |
| 801 | 1 | |a RU |b 63413507 |c 20100831 | |
| 801 | 2 | |a RU |b 63413507 |c 20120523 |g RCR | |
| 942 | |c CR | ||