Low-temperature synthesis of granular glass from mixes based on silica-alumina-containing components for obtaining foam materials
| Parent link: | Glass and Ceramics.— , 2009 Vol. 66, N 9-10.— 2009.— P. 341-344 |
|---|---|
| Weitere Verfasser: | , , , |
| Zusammenfassung: | It is established that granular glass can be obtained as an intermediate product for foam glass crystal materials based on common silica component (marshallite, diatomite, opoka) at temperatures not exceeding 900°C. It is shown that the use of granular glass with glass phase present in amounts greater than 80 wt.% makes it possible to obtain foam crystal glass materials with density up to 250 g/cm3 В фонде НТБ ТПУ отсутствует |
| Sprache: | Englisch |
| Veröffentlicht: |
2009
|
| Schlagworte: | |
| Format: | Buchkapitel |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=595996 |
| Zusammenfassung: | It is established that granular glass can be obtained as an intermediate product for foam glass crystal materials based on common silica component (marshallite, diatomite, opoka) at temperatures not exceeding 900°C. It is shown that the use of granular glass with glass phase present in amounts greater than 80 wt.% makes it possible to obtain foam crystal glass materials with density up to 250 g/cm3 В фонде НТБ ТПУ отсутствует |
|---|