Using quartzofeldspathic waste to obtain foamed glass material; Resource-Efficient Technologies; Vol. 2, Iss. 1
| Parent link: | Resource-Efficient Technologies: electronic scientific journal/ National Research Tomsk Polytechnic University (TPU).— , 2015-.— 2405-6537 Vol. 2, Iss. 1.— 2016.— [P. 23-29] |
|---|---|
| Yazar: | |
| Müşterek Yazar: | |
| Diğer Yazarlar: | , |
| Özet: | Title screen The present paper proposes a method for the processing of mine refuse non-ferrous metal ore in the production of foamed glass. The subject of this research is a low-temperature frit synthesis (<900 °C), allowing for the high-temperature glass melting process to be avoided. The technology for the production of frit without complete melting of the batch and without using glass-making units offers a considerable reduction in energy consumption and air pollution. It was found that material samples obtained with a density of up to 250 kg/m3 are of rigidity (up to 1.7 MPa) in comparison with the conventional foamed glass (1 MPa). This increased rigidity was due to the presence of crystalline phase particles in its interpore partition of less than 2 µm in size. Material with a density of 300 kg/cm3 is recommended for thermal insulation for the industrial and construction sectors. At densities above 300 kg/cm3 and a strength of 2.5 MPa, the purpose becomes heat-insulating construction material. The proposed method for obtaining a porous material from waste widens our choice of raw materials for foamed glass, whilst saving resources and energy. |
| Dil: | İngilizce |
| Baskı/Yayın Bilgisi: |
2016
|
| Konular: | |
| Online Erişim: | http://earchive.tpu.ru/handle/11683/50239 |
| Materyal Türü: | Elektronik Kitap Bölümü |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=565822 |
MARC
| LEADER | 00000naa2a2200000 4500 | ||
|---|---|---|---|
| 001 | 565822 | ||
| 005 | 20240209133728.0 | ||
| 035 | |a (RuTPU)RU\TPU\prd\262180 | ||
| 035 | |a RU\TPU\prd\262179 | ||
| 090 | |a 565822 | ||
| 100 | |a 20160908a2016 k y0rusy50 ba | ||
| 101 | 0 | |a eng | |
| 102 | |a RU | ||
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Using quartzofeldspathic waste to obtain foamed glass material |f O. V. Kazmina, A.Y. Tokareva, V. I. Vereshchagin (Vereschagin, Vereshagin) | |
| 203 | |a Text |c electronic | ||
| 300 | |a Title screen | ||
| 320 | |a [References: p. 29 (15 tit.)] | ||
| 330 | |a The present paper proposes a method for the processing of mine refuse non-ferrous metal ore in the production of foamed glass. The subject of this research is a low-temperature frit synthesis (<900 °C), allowing for the high-temperature glass melting process to be avoided. The technology for the production of frit without complete melting of the batch and without using glass-making units offers a considerable reduction in energy consumption and air pollution. It was found that material samples obtained with a density of up to 250 kg/m3 are of rigidity (up to 1.7 MPa) in comparison with the conventional foamed glass (1 MPa). This increased rigidity was due to the presence of crystalline phase particles in its interpore partition of less than 2 µm in size. Material with a density of 300 kg/cm3 is recommended for thermal insulation for the industrial and construction sectors. At densities above 300 kg/cm3 and a strength of 2.5 MPa, the purpose becomes heat-insulating construction material. The proposed method for obtaining a porous material from waste widens our choice of raw materials for foamed glass, whilst saving resources and energy. | ||
| 461 | 1 | |0 (RuTPU)RU\TPU\prd\247369 |x 2405-6537 |t Resource-Efficient Technologies |o electronic scientific journal |f National Research Tomsk Polytechnic University (TPU) |d 2015- | |
| 463 | 1 | |0 (RuTPU)RU\TPU\prd\262176 |t Vol. 2, Iss. 1 |v [P. 23-29] |d 2016 | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a фритта | |
| 610 | 1 | |a пеностекло | |
| 610 | 1 | |a плавление | |
| 610 | 1 | |a стекло | |
| 700 | 1 | |a Kazmina |b O. V. |c Chemical Engineer |c Professor of Tomsk Polytechnic University, Doctor of technical sciences |f 1967- |g Olga Viktorovna |3 (RuTPU)RU\TPU\pers\33001 |9 16846 | |
| 701 | 1 | |a Tokareva |b A.Y. | |
| 701 | 1 | |a Vereshchagin (Vereschagin, Vereshagin) |b V. I. |c Chemical Engineer |c Professor of Tomsk Polytechnic University, Doctor of technical sciences |f 1942- |g Vladimir Ivanovich |3 (RuTPU)RU\TPU\pers\26325 |9 12080 | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет (ТПУ) |b Институт физики высоких технологий (ИФВТ) |b Кафедра технологии силикатов и наноматериалов (ТСН) |3 (RuTPU)RU\TPU\col\18694 |
| 801 | 1 | |a RU |b 63413507 |c 20090623 |g PSBO | |
| 801 | 2 | |a RU |b 63413507 |c 20180830 |g PSBO | |
| 856 | 4 | |u http://earchive.tpu.ru/handle/11683/50239 | |
| 942 | |c BK | ||