Thin calcium phosphate coating deposited on NiTi and Ti

Thin calcium phosphate coating deposited on NiTi and Ti

Dades bibliogràfiques
Parent link:Koval, N. N. (specialist in the field of electronics ; 1948-). 9th International Conference on Modification of Materials with Particle Beams and Plasma Flows, Tomsk, 21-21September 2008=[9 Международная конференция по модификации материалов пучками частиц и плазменными потоками, Томск, 21-26 сентября 2008 г.]: proceedings. P. 543-546.— .— Tomsk: Publishing house of the IAO SB RAS.— 9785944580900
Altres autors: Ryabtseva M. A. Maria Alexandrovna, Surmenev R. A. Roman Anatolievich, Pichugin V. F. Vladimir Fyodorovich, Tverdokhlebov S. I. Sergei Ivanovich
Sumari:Calcium phosphate coatings with the thickness of up to 2.7 micron were deposited by rfmagnetron sputtering. Scanning electron microscopy, nanohardness technique, adhesion test,atomic absorption spectroscopy were used to study the properties of the coatings. The coatings thickness was determined by mechanical profilometry method. The nanohardness and Young's modulus of calcium phosphate coating are 10 and 110 GPa, respectively. The adhesion strength of the calcium phosphate coating to metallic substrates depended on the coating's thickness and decreased for a thickness more than 1.6 μm. No difference was observed between NiTi and Ti substrates. Calciumphosphate coating on the NiTi surface promoted a decrease in nickel release rate, which depended on the rf-power applied
Idioma:anglès
Publicat:
Matèries:
труды учёных ТПУ
Format: Capítol de llibre
KOHA link:https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=239489

Ítems similars

Ítems similars