Характер разрушения поверхности керамики В4С при локальных нагружениях; Перспективы развития фундаментальных наук
| Parent link: | Перспективы развития фундаментальных наук.— 2012.— [С. 200-202] |
|---|---|
| Main Author: | |
| Other Authors: | , , , |
| Summary: | Заглавие с экрана This article describes the experimental results of ceramic surface fracture pattern of b4c during vickers hardness and crack growth test in conditions of various loading (4,91?294,3 n). Ceramics made from boron carbide powder with addition of 10% submicron fraction of the same powder by spark plasma sintering method in different modes of sintering was studied. a complex pattern of specimen surface deformation and deterioration with the formation of chips and material delamination areas between radial fractures was observ. |
| Language: | Russian |
| Published: |
2012
|
| Series: | Физика |
| Subjects: | |
| Online Access: | http://www.lib.tpu.ru/fulltext/c/2012/C21/064.pdf |
| Format: | Electronic Book Chapter |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=237200 |
| Physical Description: | 1 файл(441 Кб) |
|---|---|
| Summary: | Заглавие с экрана This article describes the experimental results of ceramic surface fracture pattern of b4c during vickers hardness and crack growth test in conditions of various loading (4,91?294,3 n). Ceramics made from boron carbide powder with addition of 10% submicron fraction of the same powder by spark plasma sintering method in different modes of sintering was studied. a complex pattern of specimen surface deformation and deterioration with the formation of chips and material delamination areas between radial fractures was observ. |