Research of Protective Properties of Microplasma Coatings
| Parent link: | 7 International conference on modification of materials with particle beams and plasma flows: Tomsk, Russia, 25-29 July 2004/ edited by S. Korovin, A. Ryabchikov. [P. 456-458].— , 2004 |
|---|---|
| Автор: | |
| Інші автори: | , |
| Резюме: | Title from the title-page. The results of the heat resistance research of MAO - coatings are presented. The coatings were formed in the electrolytes developed earlier. For an estimation of influence on heat resistance of the coatings in compounds of the transitive metals (Co, Cu), and also ZrO2 were added into the electrolytes. It was found that at the temperature of 310 °C all the obtained coatings have strong coupling with the metal surface. An increase in the test temperature up to 500 °C showed that the silicate coating has the greatest heat resistance. It was shown that the participation of zirconium oxide at the formation of the coatings has an positive effect on its heat resistance. Режим доступа: из корпоративной сети ТПУ Text files |
| Опубліковано: |
2004
|
| Серія: | Coating deposition |
| Предмети: | |
| Онлайн доступ: | http://www.lib.tpu.ru/fulltext2/c/2004/C13/050.pdf |
| Формат: | Електронний ресурс Частина з книги |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=232131 |
| Резюме: | Title from the title-page. The results of the heat resistance research of MAO - coatings are presented. The coatings were formed in the electrolytes developed earlier. For an estimation of influence on heat resistance of the coatings in compounds of the transitive metals (Co, Cu), and also ZrO2 were added into the electrolytes. It was found that at the temperature of 310 °C all the obtained coatings have strong coupling with the metal surface. An increase in the test temperature up to 500 °C showed that the silicate coating has the greatest heat resistance. It was shown that the participation of zirconium oxide at the formation of the coatings has an positive effect on its heat resistance. Режим доступа: из корпоративной сети ТПУ Text files |
|---|