Thin structure of steel St52, 3N and possible reasons of defect of large-capacity billets AT "YURMASH"; Bulletin of the Tomsk Polytechnic University; Vol. 311, № 4 : Power engineering
| Parent link: | Bulletin of the Tomsk Polytechnic University/ Tomsk Polytechnic University (TPU).— , 2006-2007 Vol. 311, № 4 : Power engineering.— 2007.— [P. 64-69] |
|---|---|
| Daljnji autori: | , , , |
| Sažetak: | Заглавие с титульного листа Электронная версия печатной публикации Electron-microscopic and x-ray investigations of structurally-phase and intense-deformed condition of material made of defective and conditional forged billet at «Yurmash» have been carried out. It is ascertained that in steel made from the defective forged piece the fraction of perlite is 1,5...2 times higher and lamellar perlite prevails. Local long-range tensions in both conditions of material are commensurable with fluidity limit. The content of sulfides is considerably higher in the steel made from the defective billet. They are located in the body of ferrite grains and along the interfaces. In the material made from the conditional forging they are located only inside of grains. The scalar density of dislocations in ferrite grains and in ferrite layers of perlite of the defected billet is one and a half time higher than in conditional metal. All the totality of the listed above circumstances allows stating that the main cause of cracking of large-capacity billets made of steel St52, 3N is not a full conformity of the chemical compound to branded requirements. |
| Jezik: | engleski |
| Izdano: |
2007
|
| Serija: | Power engineering |
| Teme: | |
| Online pristup: | http://www.lib.tpu.ru/fulltext/v/Bulletin_TPU/2007/v311eng/i4/14.pdf |
| Format: | Elektronički Poglavlje knjige |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=194285 |
MARC
| LEADER | 00000nla2a2200000 4500 | ||
|---|---|---|---|
| 001 | 194285 | ||
| 005 | 20231101224537.0 | ||
| 035 | |a (RuTPU)RU\TPU\book\211903 | ||
| 035 | |a RU\TPU\book\211889 | ||
| 090 | |a 194285 | ||
| 100 | |a 20110411d2007 k y0rusy50 ca | ||
| 101 | 1 | |a eng |c rus | |
| 102 | |a RU | ||
| 135 | |a drnn ---uucaa | ||
| 200 | 1 | |a Thin structure of steel St52, 3N and possible reasons of defect of large-capacity billets AT "YURMASH" |b Electronic resource |f V. I. Danilov [et al.] | |
| 203 | |a Text |c electronic | ||
| 215 | |a 1 файл (17.9 Мб) | ||
| 225 | 1 | |a Power engineering | |
| 230 | |a Электронные текстовые данные (1 файл : 17.9 Мб) | ||
| 300 | |a Заглавие с титульного листа | ||
| 300 | |a Электронная версия печатной публикации | ||
| 320 | |a [Bibliography: p. 69 (7 titles)] | ||
| 330 | |a Electron-microscopic and x-ray investigations of structurally-phase and intense-deformed condition of material made of defective and conditional forged billet at «Yurmash» have been carried out. It is ascertained that in steel made from the defective forged piece the fraction of perlite is 1,5...2 times higher and lamellar perlite prevails. Local long-range tensions in both conditions of material are commensurable with fluidity limit. The content of sulfides is considerably higher in the steel made from the defective billet. They are located in the body of ferrite grains and along the interfaces. In the material made from the conditional forging they are located only inside of grains. The scalar density of dislocations in ferrite grains and in ferrite layers of perlite of the defected billet is one and a half time higher than in conditional metal. All the totality of the listed above circumstances allows stating that the main cause of cracking of large-capacity billets made of steel St52, 3N is not a full conformity of the chemical compound to branded requirements. | ||
| 337 | |a Adobe Reader | ||
| 461 | 1 | |0 (RuTPU)RU\TPU\book\169973 |t Bulletin of the Tomsk Polytechnic University |f Tomsk Polytechnic University (TPU) |d 2006-2007 | |
| 463 | 1 | |0 (RuTPU)RU\TPU\book\200683 |t Vol. 311, № 4 : Power engineering |v [P. 64-69] |d 2007 |p 146 p. | |
| 610 | 1 | |a thin structure | |
| 610 | 1 | |a steels | |
| 610 | 1 | |a defects | |
| 610 | 1 | |a large-capacity billets | |
| 610 | 1 | |a x-ray investigations | |
| 610 | 1 | |a electron-microscopic investigations | |
| 610 | 1 | |a structural-phase states | |
| 610 | 1 | |a intense-deformed condition | |
| 610 | 1 | |a materials | |
| 610 | 1 | |a forged billet | |
| 610 | 1 | |a forgings | |
| 610 | 1 | |a perlites | |
| 610 | 1 | |a fluidity | |
| 610 | 1 | |a defective blanks | |
| 610 | 1 | |a sulfides | |
| 610 | 1 | |a ferritic grain | |
| 610 | 1 | |a conditioning metals | |
| 610 | 1 | |a cracking | |
| 610 | 1 | |a chemical composition | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a электронный ресурс | |
| 675 | |a 620.18:669.14 |v 3 | ||
| 701 | 1 | |a Danilov |b V. I. |c физик |c профессор Юргинского технологического института (филиала) Томского политехнического университета, доктор физико-математических наук |f 1947- |g Владимир Иванович |2 stltpush |3 (RuTPU)RU\TPU\pers\24230 | |
| 701 | 1 | |a Valuev |b D. V. |c specialist in the field of metal working |c Associate Professor of Yurga technological Institute of Tomsk Polytechnic University, Candidate of technical sciences |f 1980- |g Denis Viktorovich |2 stltpush |3 (RuTPU)RU\TPU\pers\32900 |9 16748 | |
| 701 | 1 | |a Ivanov |b Yu. F. |c physicist |c Professor of Tomsk Polytechnic University, Doctor of physical and mathematical sciences |f 1955- |g Yuriy Fedorovich |2 stltpush |3 (RuTPU)RU\TPU\pers\33559 | |
| 701 | 1 | |a Apasov |b A. M. |c specialist in the field of material science |c Associate Professor of Yurga technological Institute of Tomsk Polytechnic University, Candidate of technical sciences |f 1950- |g Aleksandr Mikhailovich |2 stltpush |3 (RuTPU)RU\TPU\pers\35175 |9 18441 | |
| 801 | 1 | |a RU |b 63413507 |c 20090623 |g PSBO | |
| 801 | 2 | |a RU |b 63413507 |c 20160726 |g PSBO | |
| 856 | 4 | |u http://www.lib.tpu.ru/fulltext/v/Bulletin_TPU/2007/v311eng/i4/14.pdf | |
| 942 | |c CF | ||