Change of the spring Сr-Ni alloy microstructure after ageing; Bulletin of the Tomsk Polytechnic University; Vol. 311, № 2

Change of the spring Сr-Ni alloy microstructure after ageing; Bulletin of the Tomsk Polytechnic University; Vol. 311, № 2

Bibliographic Details
Parent link:Bulletin of the Tomsk Polytechnic University/ Tomsk Polytechnic University (TPU).— , 2006-2007
Vol. 311, № 2.— 2007.— [P. 110-113]
Other Authors: Skakov M. K., Mukazhanov E. B., Erbolatuly D., Isaeva Zh. M.
Summary:Заглавие с титульного листа
Электронная версия печатной публикации
It has been stated that ageing of the tempered alloy 47ХНМ at temperature 500 °С during 5...10 h does not result in disintegration of oversaturated firm solution, at ageing temperature rise up to 600 °C attributes of disintegration in particles of α-phase of homogeneoustype start to be shown. It was shown that after tempered samples ageing at 700 °C the faltering disintegration with allocation of not coherent α-phase on the basis of chrome develops intensively, and its volume fraction increases with increase in ageing time reaching the maximal values in 5...10 h of ageing
Language:English
Published: 2007
Series:Mathematics and mechanics.Physics
Subjects:
microstructures
spring alloys
ageing
temperature
disintegration
oversaturated firm solution
particles
homogeneoustype
samples
chrome
электронный ресурс
Online Access:http://www.lib.tpu.ru/fulltext/v/Bulletin_TPU/2007/v311eng/i2/28.pdf
Format: Electronic Book Chapter
KOHA link:https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=182950

Similar Items

Similar Items