Change of the spring Сr-Ni alloy microstructure after ageing
| Parent link: | Bulletin of the Tomsk Polytechnic University/ Tomsk Polytechnic University (TPU).— , 2006-2007 Vol. 311, № 2.— 2007.— [P. 110-113] |
|---|---|
| Kolejni autorzy: | , , , |
| Streszczenie: | Заглавие с титульного листа Электронная версия печатной публикации It has been stated that ageing of the tempered alloy 47ХНМ at temperature 500 °С during 5...10 h does not result in disintegration of oversaturated firm solution, at ageing temperature rise up to 600 °C attributes of disintegration in particles of α-phase of homogeneoustype start to be shown. It was shown that after tempered samples ageing at 700 °C the faltering disintegration with allocation of not coherent α-phase on the basis of chrome develops intensively, and its volume fraction increases with increase in ageing time reaching the maximal values in 5...10 h of ageing |
| Język: | angielski |
| Wydane: |
2007
|
| Seria: | Mathematics and mechanics.Physics |
| Hasła przedmiotowe: | |
| Dostęp online: | http://www.lib.tpu.ru/fulltext/v/Bulletin_TPU/2007/v311eng/i2/28.pdf |
| Format: | Elektroniczne Rozdział |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=182950 |
MARC
| LEADER | 00000nla2a2200000 4500 | ||
|---|---|---|---|
| 001 | 182950 | ||
| 005 | 20231031171430.0 | ||
| 035 | |a (RuTPU)RU\TPU\book\198323 | ||
| 035 | |a RU\TPU\book\198114 | ||
| 090 | |a 182950 | ||
| 100 | |a 20100629d2007 k y0rusy50 ca | ||
| 101 | 1 | |a eng |c rus | |
| 102 | |a RU | ||
| 135 | |a drnn ---uucaa | ||
| 200 | 1 | |a Change of the spring Сr-Ni alloy microstructure after ageing |b Electronic resource |f M. K. Skakov [et al.] | |
| 203 | |a Text |c electronic | ||
| 215 | |a 1 файл (1.1 Мб) | ||
| 225 | 1 | |a Mathematics and mechanics.Physics | |
| 230 | |a Электронные текстовые данные (1 файл : 1.1 Мб) | ||
| 300 | |a Заглавие с титульного листа | ||
| 300 | |a Электронная версия печатной публикации | ||
| 320 | |a [Bibliography: p. 113 (5 titles)] | ||
| 330 | |a It has been stated that ageing of the tempered alloy 47ХНМ at temperature 500 °С during 5...10 h does not result in disintegration of oversaturated firm solution, at ageing temperature rise up to 600 °C attributes of disintegration in particles of α-phase of homogeneoustype start to be shown. It was shown that after tempered samples ageing at 700 °C the faltering disintegration with allocation of not coherent α-phase on the basis of chrome develops intensively, and its volume fraction increases with increase in ageing time reaching the maximal values in 5...10 h of ageing | ||
| 337 | |a Adobe Reader | ||
| 461 | 1 | |0 (RuTPU)RU\TPU\book\169973 |t Bulletin of the Tomsk Polytechnic University |f Tomsk Polytechnic University (TPU) |d 2006-2007 | |
| 463 | 1 | |0 (RuTPU)RU\TPU\book\197892 |x 1684-8519 |t Vol. 311, № 2 |v [P. 110-113] |d 2007 |p 153 p. | |
| 610 | 1 | |a microstructures | |
| 610 | 1 | |a spring alloys | |
| 610 | 1 | |a ageing | |
| 610 | 1 | |a temperature | |
| 610 | 1 | |a disintegration | |
| 610 | 1 | |a oversaturated firm solution | |
| 610 | 1 | |a particles | |
| 610 | 1 | |a homogeneoustype | |
| 610 | 1 | |a samples | |
| 610 | 1 | |a chrome | |
| 610 | 1 | |a электронный ресурс | |
| 675 | |a 538.9:621.785.6 |v 3 | ||
| 701 | 1 | |a Skakov |b M. K. | |
| 701 | 1 | |a Mukazhanov |b E. B. | |
| 701 | 1 | |a Erbolatuly |b D. | |
| 701 | 1 | |a Isaeva |b Zh. M. | |
| 801 | 1 | |a RU |b 63413507 |c 20090623 |g PSBO | |
| 801 | 2 | |a RU |b 63413507 |c 20120418 |g PSBO | |
| 856 | 4 | |u http://www.lib.tpu.ru/fulltext/v/Bulletin_TPU/2007/v311eng/i2/28.pdf | |
| 942 | |c CF | ||