Change of the spring Сr-Ni alloy microstructure after ageing; Bulletin of the Tomsk Polytechnic University; Vol. 311, № 2
| Parent link: | Bulletin of the Tomsk Polytechnic University/ Tomsk Polytechnic University (TPU).— , 2006-2007 Vol. 311, № 2.— 2007.— [P. 110-113] |
|---|---|
| Diğer Yazarlar: | , , , |
| Özet: | Заглавие с титульного листа Электронная версия печатной публикации It has been stated that ageing of the tempered alloy 47ХНМ at temperature 500 °С during 5...10 h does not result in disintegration of oversaturated firm solution, at ageing temperature rise up to 600 °C attributes of disintegration in particles of α-phase of homogeneoustype start to be shown. It was shown that after tempered samples ageing at 700 °C the faltering disintegration with allocation of not coherent α-phase on the basis of chrome develops intensively, and its volume fraction increases with increase in ageing time reaching the maximal values in 5...10 h of ageing |
| Dil: | İngilizce |
| Baskı/Yayın Bilgisi: |
2007
|
| Seri Bilgileri: | Mathematics and mechanics.Physics |
| Konular: | |
| Online Erişim: | http://www.lib.tpu.ru/fulltext/v/Bulletin_TPU/2007/v311eng/i2/28.pdf |
| Materyal Türü: | Elektronik Kitap Bölümü |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=182950 |
| Fiziksel Özellikler: | 1 файл (1.1 Мб) |
|---|---|
| Özet: | Заглавие с титульного листа Электронная версия печатной публикации It has been stated that ageing of the tempered alloy 47ХНМ at temperature 500 °С during 5...10 h does not result in disintegration of oversaturated firm solution, at ageing temperature rise up to 600 °C attributes of disintegration in particles of α-phase of homogeneoustype start to be shown. It was shown that after tempered samples ageing at 700 °C the faltering disintegration with allocation of not coherent α-phase on the basis of chrome develops intensively, and its volume fraction increases with increase in ageing time reaching the maximal values in 5...10 h of ageing |