The Use of the Ultrasonic Compaction Method for the PZT Piezoelectric Ceramics Fabrication; Korus 99; The 3th Russia-Korean International Symposium on Science and Technology; Vol. 2: Proceedings
| Parent link: | Korus 99.— , 1999 The 3th Russia-Korean International Symposium on Science and Technology: June 22 - 25, 1999, Tomsk/ Tomsk Polytechnic University (TPU) ; Novosibirsk State Technical University Vol. 2: Proceedings.— 1999.— P. 557-560 |
|---|---|
| Beste egile batzuk: | , , , , , , |
| Gaia: | The method of ultrasonic (US) compaction for the fabrication of Pb(ZrTi)O3 PZT piezoceramics was approved. The values of density, granularity, shrinkage of ceramic samples, sintered from the compacts compacted by traditional uniaxial pressing and by ultrasound action are compared. It is shown that US compaction contributes to sintering temperature lowering and to PZT piezoceramics granularity reduction |
| Hizkuntza: | ingelesa |
| Argitaratua: |
1999
|
| Gaiak: | |
| Formatua: | Liburu kapitulua |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=167586 |
| Gaia: | The method of ultrasonic (US) compaction for the fabrication of Pb(ZrTi)O3 PZT piezoceramics was approved. The values of density, granularity, shrinkage of ceramic samples, sintered from the compacts compacted by traditional uniaxial pressing and by ultrasound action are compared. It is shown that US compaction contributes to sintering temperature lowering and to PZT piezoceramics granularity reduction |
|---|